Color |
Grade |
Hardness (Shore A) |
Hardness (Shore D) |
MFR (g/10min) @230℃ |
MFR (g/10min) @230℃ |
Density (kg/m2) |
Modulus (Mpa) |
TS at break |
Elongation |
ISO 48 |
ISO 48 |
2.16 kg.
ISO 1133 |
10 kg.
ISO 1133 |
ASTM D1505 |
ISO 37 |
(Mpa)
ISO 37 |
(%)
ISO 37 |
Black |
5020BS |
|
|
|
|
|
|
|
|
5030BS |
|
|
|
|
|
|
|
|
6020BS |
|
|
|
|
|
|
|
|
6030BS |
56 |
– |
– |
30 |
880 |
1.4 |
3.8 |
480 |
7030BS |
66 |
– |
– |
35 |
880 |
2.4 |
5.3 |
440 |
8032BS |
79 |
– |
– |
15 |
890 |
3.2 |
7.1 |
580 |
8030BS |
86 |
– |
– |
15 |
890 |
4.5 |
8.6 |
580 |
9020BS |
89 |
– |
– |
10 |
890 |
5.7 |
7.5 |
500 |
9070BKS |
– |
38 |
20 |
– |
890 |
8.2 |
13.2 |
640 |
M4400BS |
|
|
|
|
|
|
|
|
W600B |
55 |
– |
– |
54 |
880 |
1.6 |
5.5 |
520 |
W700B |
67 |
– |
– |
30 |
880 |
2.5 |
5.6 |
450 |
W750B |
73 |
– |
– |
45 |
880 |
2.8 |
6.8 |
550 |
W800B |
77 |
– |
– |
18 |
880 |
3.4 |
8.5 |
600 |
C700BM |
|
|
|
|
|
|
|
|
C800BM |
|
|
|
|
|
|
|
|
G750BS |
|
|
|
|
|
|
|
|
G800BS |
79 |
– |
1 |
– |
880 |
3.0 |
5.9 |
550 |
S-250B |
16 |
– |
2 |
– |
880 |
0.4 |
1.5 |
500 |
S-450B |
40 |
– |
1 |
– |
880 |
1.1 |
2.6 |
360 |
8051BS |
86 |
– |
35 |
– |
890 |
5.2 |
7.9 |
440 |
A500B |
54 |
– |
– |
23 |
880 |
1.5 |
3.9 |
300 |
A600B |
62 |
– |
– |
20 |
880 |
2.1 |
4.5 |
250 |
A700B |
72 |
– |
– |
20 |
880 |
3.0 |
7.0 |
330 |
A750B |
80 |
– |
– |
48 |
880 |
4.0 |
8.2 |
370 |
A800B |
78 |
– |
– |
45 |
880 |
3.5 |
8.7 |
380 |
A900B |
90 |
– |
– |
45 |
880 |
4.9 |
10.0 |
480 |
A950B |
– |
33 |
– |
110 |
890 |
7.1 |
13.6 |
440 |
A970B |
– |
42 |
– |
50 |
900 |
9.6 |
17.7 |
550 |
Natural |
5031NHS |
58 |
– |
– |
5 |
880 |
1.5 |
5.4 |
600 |
6030NS |
53 |
– |
– |
50 |
880 |
1.4 |
3.4 |
450 |
7030NS |
68 |
– |
– |
30 |
880 |
2.3 |
6.1 |
580 |
7060NS |
75 |
– |
– |
42 |
870 |
3.0 |
8.4 |
580 |
8030NHS |
84 |
– |
– |
9 |
880 |
4.6 |
8.1 |
520 |
8030NS |
83 |
– |
– |
15 |
880 |
4.2 |
8.2 |
590 |
8032NS |
77 |
– |
– |
15 |
880 |
3.3 |
6.7 |
520 |
9020NS |
89 |
– |
– |
10 |
890 |
5.4 |
6.6 |
560 |
M4400NS |
– |
46 |
0.5 |
– |
890 |
10.4 |
17.8 |
650 |
Note :
Click “Grade Name” to more detail
All of the above listed data are representative values, and not specific ones.
Milastomer™ is a light-weight, soft resin with low density and excellent moldability. Demand has grown significantly for uses in automotive materials, gaskets and civil engineering joint fillers, building materials, and grips, and is expected to continue to expand around the world in line with wider uses in automotive interiors and as weather strips. The planned production facilities augmentation for Milastomer™ is a proactive response to such demands